Fundamental investigation of ultrasonic-assisted metal forming by compressive and shear stress
Third party funded individual grant
Start date : 01.03.2018
End date : 30.11.2022
Project details
Short description
One approach to extend the process limits in bulk forming is to superimpose a high-frequency oscillation on the tool movement. This so-called ultrasonic assistance (US) leads to an immediate reduction of the material's flow stress and therefore to decreased tool and workpiece loads. The research project is focused on the underlying mechanisms of the flow stress reduction and the effects on the material flow behavior. In oscillation superimposed shear tests, it was found that the cyclic loading and unloading promotes the crack initiation and thus leads to earlier material failure. Hence, the formability of the material C35E is reduced by the ultrasonic assistance.
Scientific Abstract
Ein Ansatz die Prozessgrenzen in der Massivumformung zu erweitern, ist die Überlagerung der Werkzeugbewegung mit einer hochfrequenten Oszillation. Diese sogenannte Ultraschallunterstützung (US) führt zu einer unmittelbaren Reduzierung der Fließspannung und damit zu verringerten Werkzeug- und Werkstückbelastungen. Der Fokus der grundlagenwissenschaftlichen Untersuchungen in diesem Projekt liegt auf den zugrundeliegenden Mechanismen der Fließspannungsreduktion sowie der Auswirkungen auf das Werkstoffflussverhalten. In schwingungsüberlagerten Scherversuchen wurde ermittelt, dass die zyklische Be- und Entlastung die Rissinitiierung begünstigt und somit zu einem früheren Materialversagen führt. Das Formänderungsvermögen des Werkstoffs C35E wird somit durch die Ultraschallunterstützung verringert.