Oxidation and coordination states assumed by transition metal dopants in an invert ultrabasic silicate glass
Zandona A, Castaing V, Shames A, Helsch G, Deubener J, Becerro AI, Allix M, Goldstein A (2023)
Publication Type: Journal article
Publication year: 2023
Journal
Book Volume: 603
DOI: 10.1016/j.jnoncrysol.2022.122094
Abstract
An ultrabasic invert silicate glass (46SiO2.11Na2O.21CaO.22BaO, optical basicity index equal to 0.71) was synthesized (O2 atmosphere) and used as host for various transition metal dopants. Optical absorption, emission and electron paramagnetic spectroscopies were used to characterize oxidation and coordination states. Some of the dopants displayed only their maximal oxidation state (Ti4+, V5+, Cr6+, Mo6+ and W6+). Others exhibited mixed valences: (i) Mn3+ was the dominant species, alongside Mn2+ and Mn5+; (ii) stable Fe3+ prevailed, although some Fe2+ was preliminarily suggested by the absorption spectrum; (iii) Co3+ probably accompanied the dominant Co2+ tetrahedral oxide complex; (iv) like in "conventional" silicate glasses, only Ni2+ was detected, though simultaneously located in tetrahedral and octahedral sites (somewhat distorted); (v) Cu+ was surprisingly identified alongside the expected 6-fold coordinated Cu2+. Drastic reduction of the oxygen content in the melting atmosphere led to conversion of Cr6+ to Cr3+, despite the extreme basicity of the host.
Involved external institutions
Technische Universität Clausthal / Clausthal University of Technology
Germany (DE)
University of Seville / Universidad de Sevilla
Spain (ES)
University of Orléans / Université d'Orléans
France (FR)
Technion - Israel Institute of Technology
Israel (IL)
Ben-Gurion University of the Negev (BGU) / אוניברסיטת בן-גוריון בנגב
Israel (IL)
Germany (DE)
University of Seville / Universidad de Sevilla
Spain (ES)
University of Orléans / Université d'Orléans
France (FR)
Technion - Israel Institute of Technology
Israel (IL)
Ben-Gurion University of the Negev (BGU) / אוניברסיטת בן-גוריון בנגב
Israel (IL)
How to cite
APA:
Zandona, A., Castaing, V., Shames, A., Helsch, G., Deubener, J., Becerro, A.I.,... Goldstein, A. (2023). Oxidation and coordination states assumed by transition metal dopants in an invert ultrabasic silicate glass. Journal of Non-Crystalline Solids, 603. https://dx.doi.org/10.1016/j.jnoncrysol.2022.122094
MLA:
Zandona, Alessio, et al. "Oxidation and coordination states assumed by transition metal dopants in an invert ultrabasic silicate glass." Journal of Non-Crystalline Solids 603 (2023).
BibTeX: Download