The alloying elements Nb, Ta and Zr improve the creep properties of fully lamellar γ/α2 titanium aluminides significantly. Since high temperature deformation mainly occurs in the γ-phase of γ/α2 titanium aluminides, the diffusivity and the solid solution hardening effect of these three elements in the γ-phase is studied by analyzing the concentration gradients of the alloying elements and the resulting hardness across the interdiffusion zone of diffusion couples by energy dispersive X-ray diffraction and nanoindentation. The results reveal that Zr has the highest interdiffusion coefficient but also the largest solid solution hardening coefficient. The mechanical properties of single γ-phase Ti-54Al-5X alloys were investigated by strain rate jump tests. The addition of 5 at.% Nb or Ta lead to an increased strength compared to a binary γ-Ti-54Al alloy. The Zr-containing γ-TiAl alloy reveals the highest strength at 750°C and 900°C, which is discussed to be due to the strong solid solution hardening effect of Zr. However, in comparison to the other alloys, Ti-54Al-5Zr shows quite brittle behavior up to 900°C. The lower diffusivity of Ta compared to Nb leads to a higher strength of the Ta-modified alloy at 900◦C.
APA:
Haußmann, L., Neumeier, S., Bresler, J., Keim, S., Pyczak, F., & Göken, M. (2022). Influence of Nb, Ta and Zr on the Interdiffusion Coefficients and Solid Solution Strengthening of γ-TiAl Single Phase Alloys. Metals, 12(5). https://doi.org/10.3390/met12050752
MLA:
Haußmann, Lukas, et al. "Influence of Nb, Ta and Zr on the Interdiffusion Coefficients and Solid Solution Strengthening of γ-TiAl Single Phase Alloys." Metals 12.5 (2022).
BibTeX: Download