Nanoscale architecture of ceria-based model catalysts: Pt–Co nanostructures on well-ordered CeO2(111) thin films

Lykhach Y, Skála T, Neitzel A, Tsud N, Beranová K, Prince KC, Matolín V, Libuda J (2020)

---

Publication Type: Journal article

Publication year: 2020

Journal

Book Volume: 41

Pages Range: 985-997

Journal Issue: 6

DOI: 10.1016/S1872-2067(19)63462-5

Abstract

We have prepared and characterized atomically well-defined model systems for ceria-supported Pt–Co core–shell catalysts. Pt@Co and Co@Pt core–shell nanostructures were grown on well-ordered CeO2(111) films on Cu(111) by physical vapour deposition of Pt and Co metals in ultrahigh vacuum and investigated by means of synchrotron radiation photoelectron spectroscopy and resonant photoemission spectroscopy. The deposition of Co onto CeO2(111) yields Co–CeO2(111) solid solution at low Co coverage (0.5 ML), followed by the growth of metallic Co nanoparticles at higher Co coverages. Both Pt@Co and Co@Pt model structures are stable against sintering in the temperature range between 300 and 500 K. After annealing at 500 K, the Pt@Co nanostructure contains nearly pure Co-shell while the Pt-shell in the Co@Pt is partially covered by metallic Co. Above 550 K, the re-ordering in the near surface regions yields a subsurface Pt–Co alloy and Pt-rich shells in both Pt@Co and Co@Pt nanostructures. In the case of Co@Pt nanoparticles, the chemical ordering in the near surface region depends on the initial thickness of the deposited Pt-shell. Annealing of the Co@Pt nanostructures in the presence of O2 triggers the decomposition of Pt–Co alloy along with the oxidation of Co, regardless of the thickness of the initial Pt-shell. Progressive oxidation of Co coupled with adsorbate-induced Co segregation leads to the formation of thick CoO layers on the surfaces of the supported Co@Pt nanostructures. This process is accompanied by the disintegration of the CeO2(111) film and encapsulation of oxidized Co@Pt nanostructures by CeO2 upon annealing in O2 above 550 K. Notably, during oxidation and reduction cycles with O2 and H2 at different temperatures, the changes in the structure and chemical composition of supported Co@Pt nanostructures were driven mainly by oxidation while reduction treatments had little effect regardless of the initial thickness of the Pt-shell.

Authors with CRIS profile

Involved external institutions

How to cite

APA:

Lykhach, Y., Skála, T., Neitzel, A., Tsud, N., Beranová, K., Prince, K.C.,... Libuda, J. (2020). Nanoscale architecture of ceria-based model catalysts: Pt–Co nanostructures on well-ordered CeO2(111) thin films. Chinese Journal of Catalysis, 41(6), 985-997. https://dx.doi.org/10.1016/S1872-2067(19)63462-5

MLA:

Lykhach, Yaroslava, et al. "Nanoscale architecture of ceria-based model catalysts: Pt–Co nanostructures on well-ordered CeO2(111) thin films." Chinese Journal of Catalysis 41.6 (2020): 985-997.

BibTeX: Download