To investigate whether the formation of rafts in Co-base superalloys has a hardening or softening effect, the single crystal deformation behavior was studied in the high temperature/low stress creep regime. The large positive lattice misfit of the investigated Co-base superalloy led to a pronounced directional coarsening of the microstructure normal to the stress axis during compressive creep at 950 degrees C/150 MPa. Two creep minima were observed similar to Ni-base superalloys under tensile creep. Rafting was accompanied by a decreasing creep rate indicating a hardening effect, although cutting of gamma' rafts by partial dislocations under the formation of stacking faults occurred. (C) 2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
APA:
Xue, F., Zenk, C., Freund, L., Hoelzel, M., Neumeier, S., & Göken, M. (2018). Double minimum creep in the rafting regime of a single-crystal Co-base superalloy. Scripta Materialia, 142, 129-132. https://doi.org/10.1016/j.scriptamat.2017.08.039
MLA:
Xue, Fei, et al. "Double minimum creep in the rafting regime of a single-crystal Co-base superalloy." Scripta Materialia 142 (2018): 129-132.
BibTeX: Download