Hammer L, Ristein J, Ley L (1999)
Publication Type: Journal article
Publication year: 1999
Publisher: Elsevier
Book Volume: 443
Pages Range: 177
DOI: 10.1016/S0039-6028(99)01010-9
The atomic and electronic structures of the hydrogenated and hydrogen-free diamond (110) surface are investigated by low-energy electron diffraction (LEED), angle-resolved photoelectron spectroscopy (ARPES), and X-ray induced core-level spectroscopy (XPS). From the C 1s core-level spectra, different states of surface termination can be distinguished. The plasma-hydrogenated surface exhibits a surface C 1s component shifted by 0.8 eV towards a higher binding energy, which we attribute to coadsorbed hydrocarbons. During thermal annealing up to 900 °C, gradual desorption first of the hydrocarbons and then of hydrogen yields a clean surface with a surface C 1s component shifted by -1.1 eV and an increase in downward band bending of about 1.2 eV compared to the as-prepared surface. From the valence band spectra, we conclude that an essentially hydrogen-terminated surface is maintained at an annealing temperature of 600-800 °C. All states of the surface are unreconstructed. After the plasma treatment, the surface reveals monoatomic steps running parallel to the [11̄0] direction. From an analysis of the extinction of LEED reflexes, we conclude that within the chains of surface atoms running along [11̄0], the C-C bond length is uniformly altered in a way that keeps the chains undimerized. Finally, for the hydrogen-free surface, an occupied surface band is observed with a dispersion of 0.35 eV between Γ̄ and J̄ that lies entirely below the valence band maximum.
APA:
Hammer, L., Ristein, J., & Ley, L. (1999). The hydrogenated and bare diamond (110) surface: a combined LEED-, XPS-, and ARPES study. Surface Science, 443, 177. https://doi.org/10.1016/S0039-6028(99)01010-9
MLA:
Hammer, Lutz, Jürgen Ristein, and Lothar Ley. "The hydrogenated and bare diamond (110) surface: a combined LEED-, XPS-, and ARPES study." Surface Science 443 (1999): 177.
BibTeX: Download