Dinkel M, Heinz P, Pyczak F, Volek A, Ott M, Affeldt E, Vossberg A, Göken M, Singer R (2008)
Publication Language: English
Publication Status: Published
Publication Type: Conference contribution
Publication year: 2008
Publisher: TMS
City/Town: Warrendale
Pages Range: 211-220
Conference Proceedings Title: Superalloys 2008: Proceedings of the 11th Intenational Symposium of Superalloys
DOI: 10.7449/2008/Superalloys_2008_211_220
The solidification mechanisms and kinetics were examined and show rather distinct deviations from Transient Liquid Phase Bonding theory for binary systems due to the multicomponent diffusion in the present system. Mechanical testing was performed at room temperature via nanoindentation and at elevated temperatures by hot tensile tests. The nanoindentation results show minor differences in hardness and elastic modulus between brazing joints and parent material. Ultimate tensile strengths of more than 90 % compared to the parent material were obtained in tensile testing at 980 degrees C.
APA:
Dinkel, M., Heinz, P., Pyczak, F., Volek, A., Ott, M., Affeldt, E.,... Singer, R. (2008). New boron and silicon free single crystal-diffusion brazing alloys. In R.C. Reed, K.A. Kenneth, P. Caron, T.P. Gabb, M.G. Fahrmann, E.S. Huron, S.A. Woodard (Eds.), Superalloys 2008: Proceedings of the 11th Intenational Symposium of Superalloys (pp. 211-220). Seven Springs, US: Warrendale: TMS.
MLA:
Dinkel, Markus, et al. "New boron and silicon free single crystal-diffusion brazing alloys." Proceedings of the 11th International Symposium on Superalloys, SUPERALLOYS 2008, Seven Springs Ed. R.C. Reed, K.A. Kenneth, P. Caron, T.P. Gabb, M.G. Fahrmann, E.S. Huron, S.A. Woodard, Warrendale: TMS, 2008. 211-220.
BibTeX: Download