In-situ X-ray diffraction analysis of the recrystallization process in Cu2ZnSnS4nanoparticles synthesised by hot-injection

Brandl M, Ahmad R, Distaso M, Azimi SH, Hou Y, Peukert W, Brabec C, Hock R (2015)


Publication Language: English

Publication Status: Published

Publication Type: Journal article, Original article

Publication year: 2015

Journal

Publisher: Elsevier

Book Volume: 582

Pages Range: 269-271

DOI: 10.1016/j.tsf.2014.10.077

Abstract

Kesterite CuZnSnS(CZTS) is a promising material for thin film solar cell applications. The biggest advantages of this compound lie in the abundance and non-toxicity of the contained elements. Low temperature hot injection synthesis can provide an economic way to produce CZTS nanoparticles for application in solution processed solar cells. Powder X-ray diffraction (PXRD) measurements on the as-synthesised particles suggest that the crystal structure is cubic and can be best described as sphalerite-like. This means that the cations in the CZTS are statistically distributed on the cation sites of the crystal lattice rather than well-ordered like in the tetragonal kesterite structure. An in-situ PXRD measurement while annealing the particles up to 550 °C revealed a recrystallization process that transforms the structure from cubic to tetragonal meaning an ordering of the cations.

Authors with CRIS profile

How to cite

APA:

Brandl, M., Ahmad, R., Distaso, M., Azimi, S.H., Hou, Y., Peukert, W.,... Hock, R. (2015). In-situ X-ray diffraction analysis of the recrystallization process in Cu2ZnSnS4nanoparticles synthesised by hot-injection. Thin Solid Films, 582, 269-271. https://doi.org/10.1016/j.tsf.2014.10.077

MLA:

Brandl, Marco, et al. "In-situ X-ray diffraction analysis of the recrystallization process in Cu2ZnSnS4nanoparticles synthesised by hot-injection." Thin Solid Films 582 (2015): 269-271.

BibTeX: Download