Low temperature formation of CuIn1 - xGaxSe2solar cell absorbers by all printed multiple species nanoparticulate Se + Cu-In + Cu-Ga precursors


Publication Details
Author(s): Möckel S, Wernicke T, Arzig M, Köder P, Brandl M, Ahmad R, Distaso M, Peukert W, Hock R, Wellmann P
Publisher: Elsevier
Publication year: 2015
Volume: 582
Pages range: 60-68
ISSN: 0040-6090
Language: English

Abstract

In this work an all nanoparticulate precursor for application in Cu(InGa)Sesolar cell absorbers is presented. Binary Cu-In nanoparticles, Cu-Ga powder and elemental Se nanoparticles were mixed in dispersion and deposited on Mo-coated substrates. Research was focused on Cu(InGa)Selayer formation kinetics, phase composition characterised by differential scanning calorimetry and in-situ X-ray diffraction (XRD). Furthermore phase composition and morphology were studied by ex-situ XRD, Raman spectroscopy and scanning electron microscopy. The results revealed a fast consumption of the precursor and the formation of CuInSebelow 340 °C. Binary secondary phases were not observed at any temperature.



How to cite
APA: Möckel, S., Wernicke, T., Arzig, M., Köder, P., Brandl, M., Ahmad, R.,... Wellmann, P. (2015). Low temperature formation of CuIn1 - xGaxSe2solar cell absorbers by all printed multiple species nanoparticulate Se + Cu-In + Cu-Ga precursors. Thin Solid Films, 582, 60-68. https://dx.doi.org/10.1016/j.tsf.2014.11.060

MLA: Möckel, Stefan, et al. "Low temperature formation of CuIn1 - xGaxSe2solar cell absorbers by all printed multiple species nanoparticulate Se + Cu-In + Cu-Ga precursors." Thin Solid Films 582 (2015): 60-68.

BibTeX: Download
Share link
Last updated on 2017-09-25 at 03:13
PDF downloaded successfully