Temperature-dependent R-curve behavior of the lead-free ferroelectric 0.615Ba(Zr0.2Ti0.8)O-3-0.385(Ba0.7Ca0.3)TiO3 ceramic


Publication Details
Author(s): Voegler M, Acosta M, Brandt DRJ, Molina-Luna L, Webber K
Publisher: Elsevier
Publication year: 2015
Volume: 144
Pages range: 68-77
ISSN: 0013-7944

Abstract

The temperature-dependent crack growth resistance behavior of the lead-free (1-x)Ba(Zr0.2Ti0.8)O-3-x(Ba0.7Ca0.3)TiO3 (x = 0.385) ceramic was characterized using compact-tension specimens from 25 degrees C to 60 degrees C. The observed plateau fracture toughness at 25 degrees C was found to be approximately 37% lower than commercial Pb(Zr,Ti)O-3. At elevated temperature, the maximum fracture toughness displayed a decrease, which was found to be related to the temperature-dependent elastic and ferroelastic properties. Mechanical measurements are presented that demonstrate decreasing effective switching strain, coercive stress and Young's modulus with increasing temperature. (C) 2015 Elsevier Ltd. All rights reserved.



How to cite
APA: Voegler, M., Acosta, M., Brandt, D.R.J., Molina-Luna, L., & Webber, K. (2015). Temperature-dependent R-curve behavior of the lead-free ferroelectric 0.615Ba(Zr0.2Ti0.8)O-3-0.385(Ba0.7Ca0.3)TiO3 ceramic. Engineering Fracture Mechanics, 144, 68-77. https://dx.doi.org/10.1016/j.engfracmech.2015.06.069

MLA: Voegler, Malte, et al. "Temperature-dependent R-curve behavior of the lead-free ferroelectric 0.615Ba(Zr0.2Ti0.8)O-3-0.385(Ba0.7Ca0.3)TiO3 ceramic." Engineering Fracture Mechanics 144 (2015): 68-77.

BibTeX: Download


External Organisations
Share link
Last updated on 2017-11-24 at 02:26
PDF downloaded successfully