R-curves. in transformation toughened lead zirconate titanate


Publication Details
Author(s): Rödel J, Seo YH, Bencan A, Malic B, Kosec M, Webber K
Publisher: Elsevier
Publication year: 2013
Volume: 100
Pages range: 86-91
ISSN: 0013-7944

Abstract

Composites from lead zirconate titanate (PZT) and yttria stabilized zirconia were manufactured to assess cracking and R-curve behavior in compact tension specimens. Additions of zirconia led to a reduction in PZT grain size and shifted the fracture behavior from intergranular fracture to intragranular fracture. The R-curves exhibited higher starting values, a steeper slope and a higher plateau value with increasing content of zirconia, albeit the effects on the toughness values were not more than 20%. The results are rationalized through increased crack tip toughness, reduced ferroelastic toughening and enhanced transformation toughening. (C) 2012 Elsevier Ltd. All rights reserved.



How to cite
APA: Rödel, J., Seo, Y.-H., Bencan, A., Malic, B., Kosec, M., & Webber, K. (2013). R-curves. in transformation toughened lead zirconate titanate. Engineering Fracture Mechanics, 100, 86-91. https://dx.doi.org/10.1016/j.engfracmech.2012.06.023

MLA: Rödel, Jürgen, et al. "R-curves. in transformation toughened lead zirconate titanate." Engineering Fracture Mechanics 100 (2013): 86-91.

BibTeX: Download
Share link
Last updated on 2017-09-20 at 02:58
PDF downloaded successfully