Optimizing the Zn and Mg contents of Al–Zn–Mg wrought alloys for high strength and industrial-scale extrudability

Arnoldt A, Österreicher JA, Schiffl A, Höppel HW (2024)

Publication Type: Journal article

Publication year: 2024

Journal

Journal of Materials Research and Technology Elsevier

Book Volume: 32

Pages Range: 2972-2982

DOI: 10.1016/j.jmrt.2024.08.014

Abstract

High-strength Al alloys of the 7xxx series are promising candidates for further light-weighting of car bodies. However, they are difficult to process by extrusion: complex geometries in particular pose a major challenge due to high extrusion pressures and tool wear. In addition to process optimization, alloy chemistries can be tailored for properties such as good extrudability or high strength. In this work, several experimental alloys based on EN AW 7108A were investigated with respect to the contents of the main alloying elements Zn and Mg, as well as heat treatment (e.g., homogenization), to achieve good extrudability and favourable mechanical properties. The experimental alloys were initially extruded on a small-scale extrusion press and evaluated with regards to their warm formability, microstructure, extrudability, and mechanical properties in T5 temper. Alloy compositions with Mg contents <1.2 wt.-% are optimal and lead to good extrudability as well as high yield strengths well above 350 MPa. The Zn content, on the other hand, has minor influence on the extrudability, but significantly increases strength at higher contents (∼60 MPa). However, the combined Zn + Mg content should not exceed 7 wt.-%. Based on these findings, two optimized alloys were designed, direct chill cast on industrial scale, and extruded on an industrial extrusion press. The alloys showed good extrudability and high strength in the T5 condition. The results also reveal that the limits of the EN AW 7108A alloy are exhausted and higher strengths could only be achieved with the optimized EN AW 7003 alloy.

Authors with CRIS profile

Heinz Werner Höppel Lehrstuhl für Werkstoffwissenschaften (Allgemeine Werkstoffeigenschaften)

Involved external institutions

LKR Leichtmetallkompetenzzentrum Ranshofen GmbH AT Austria (AT) Hammerer Aluminium Industries GmbH AT Austria (AT)

How to cite

APA:

Arnoldt, A., Österreicher, J.A., Schiffl, A., & Höppel, H.W. (2024). Optimizing the Zn and Mg contents of Al–Zn–Mg wrought alloys for high strength and industrial-scale extrudability. Journal of Materials Research and Technology, 32, 2972-2982. https://doi.org/10.1016/j.jmrt.2024.08.014

MLA:

Arnoldt, Aurel, et al. "Optimizing the Zn and Mg contents of Al–Zn–Mg wrought alloys for high strength and industrial-scale extrudability." Journal of Materials Research and Technology 32 (2024): 2972-2982.

BibTeX: Download