Yielding behavior of a single-crystalline γ'-strengthened Co-Ti-Cr superalloy

Bezold A, Volz N, Lenz M, Zenk C, Spiecker E, Mills MJ, Göken M, Neumeier S (2021)


Publication Type: Journal article, Original article

Subtype: other

Publication year: 2021

Journal

Book Volume: 200

Pages Range: 113928

DOI: 10.1016/j.scriptamat.2021.113928

Abstract

The anomalous yielding behavior known from Ni3Al or Ni-base superalloys is explained by the formation of immobile dislocation configurations via cross-slip of the leading superpartial of anti-phase boundary-coupled dislocation pairs. A systematic investigation of the anomalous yielding behavior of a single-crystalline Co-11Ti-15Cr superalloy by transmission electron microscopy revealed the absence of similar sessile dislocation configurations during the initial yielding stage. Shearing of γ' precipitates via superlattice stacking fault formation is the dominant deformation mechanism at the peak temperature. Furthermore, the high density of superlattice stacking faults and their interactions also lead to a pronounced work-hardening anomaly.

Authors with CRIS profile

Additional Organisation(s)

Related research project(s)

Involved external institutions

How to cite

APA:

Bezold, A., Volz, N., Lenz, M., Zenk, C., Spiecker, E., Mills, M.J.,... Neumeier, S. (2021). Yielding behavior of a single-crystalline γ'-strengthened Co-Ti-Cr superalloy. Scripta Materialia, 200, 113928. https://dx.doi.org/10.1016/j.scriptamat.2021.113928

MLA:

Bezold, Andreas, et al. "Yielding behavior of a single-crystalline γ'-strengthened Co-Ti-Cr superalloy." Scripta Materialia 200 (2021): 113928.

BibTeX: Download