IrO2 coated TiO2 core-shell microparticles advance performance of low loading proton exchange membrane water electrolyzers

Pham CV, Bühler M, Knöppel J, Bierling M, Seeberger D, Escalera-López D, Mayrhofer K, Cherevko S, Thiele S, Thiele S (2020)

Publication Type: Journal article

Publication year: 2020

Journal

Book Volume: 269

Article Number: 118762

DOI: 10.1016/j.apcatb.2020.118762

Abstract

Herein we present novel IrO2 coated TiO2 core-shell microparticles (IrO2@TiO2) as an oxygen evolution reaction catalyst. We compare the IrO2@TiO2 catalyst to commercial TiO2 supported IrO2 catalyst (IrO2/TiO2) and pure IrO2 catalyst powder. A stability analysis via on-line inductively coupled plasma mass spectrometry based on the S-number, a descriptor considering both energy efficiency and catalyst utilization efficiency, shows that the IrO2@TiO2 catalyst shows high potential for practical applications. This was further confirmed by full-cell tests showing superior performance of the IrO2@TiO2 catalyst with moderate and low loadings of 1.2 mgIr cm⁻² and 0.4 mgIr cm⁻², respectively. The core-shell catalyst is synthesized via facile route suitable for large quantities. Moreover, stable inks from the synthesized catalyst powder make this system appealing for large scale manufacturing of cells. Given the facile synthesis route, high activity, and good stability, the IrO2@TiO2 catalyst is potentially suitable for industry proton exchange membrane water electrolysis application.

Authors with CRIS profile

Involved external institutions

Forschungszentrum Jülich / Research Centre Jülich (FZJ) Germany (DE) Albert-Ludwigs-Universität Freiburg Germany (DE)

How to cite

APA:

Pham, C.V., Bühler, M., Knöppel, J., Bierling, M., Seeberger, D., Escalera-López, D.,... Thiele, S. (2020). IrO2 coated TiO2 core-shell microparticles advance performance of low loading proton exchange membrane water electrolyzers. Applied Catalysis B-Environmental, 269. https://dx.doi.org/10.1016/j.apcatb.2020.118762

MLA:

Pham, Chuyen Van, et al. "IrO2 coated TiO2 core-shell microparticles advance performance of low loading proton exchange membrane water electrolyzers." Applied Catalysis B-Environmental 269 (2020).

BibTeX: Download