Oxidation Behavior of Superalloy IN 713 Fabricated by Metal Injection Molding

Beitrag in einer Fachzeitschrift
(Originalarbeit)


Details zur Publikation

Autor(en): Sheng N, Horke K, Meyer A, Rettig R, Singer R
Zeitschrift: Oxidation of Metals
Verlag: Springer New York LLC
Jahr der Veröffentlichung: 2018
ISSN: 0030-770X
Sprache: Englisch


Abstract

The oxidation behavior of superalloy IN 713 fabricated by metal
injection molding (MIM) was investigated and compared with standard cast
material plus hot isostatic pressing (Cast + HIP). The carbon content
of MIM alloys varied in the experiments due to the use of different
starting powders. At all temperatures and times investigated, weight
gain increased strongly with carbon content. Carbon in the alloys was
present mainly in the form of carbides. Carbides react with oxygen
during oxide scale formation. Microscopy showed that selective oxidation
of carbides led to the formation of protrusions and cracks in the oxide
layer. In this way, the protective effect of the oxide scale was
weakened.



FAU-Autoren / FAU-Herausgeber

Horke, Katharina
Zentralinstitut für Neue Materialien und Prozesstechnik
Meyer, Andreas
Zentralinstitut für Neue Materialien und Prozesstechnik
Rettig, Ralf Dr.-Ing.
Lehrstuhl für Werkstoffwissenschaften (Werkstoffkunde und Technologie der Metalle)
Sheng, Naicheng Dr.
Zentralinstitut für Neue Materialien und Prozesstechnik
Singer, Robert Prof. Dr.-Ing.
Lehrstuhl für Werkstoffwissenschaften (Werkstoffkunde und Technologie der Metalle)


Zitierweisen

APA:
Sheng, N., Horke, K., Meyer, A., Rettig, R., & Singer, R. (2018). Oxidation Behavior of Superalloy IN 713 Fabricated by Metal Injection Molding. Oxidation of Metals. https://dx.doi.org/10.1007/s11085-018-9869-y

MLA:
Sheng, Naicheng, et al. "Oxidation Behavior of Superalloy IN 713 Fabricated by Metal Injection Molding." Oxidation of Metals (2018).

BibTeX: 

Zuletzt aktualisiert 2018-22-11 um 13:50