In-situ phase formation study of copper indium diselenide absorber layers from CuIn nanoparticles and evaporated selenium

Beitrag in einer Fachzeitschrift


Details zur Publikation

Autorinnen und Autoren: Möckel S, Hölzing A, Hock R, Wellmann P
Zeitschrift: Thin Solid Films
Verlag: Elsevier
Jahr der Veröffentlichung: 2013
Band: 535
Heftnummer: 1
Seitenbereich: 133-137
ISSN: 0040-6090
Sprache: Englisch


Abstract


In this work CuInSe (CISe) thin films were fabricated by rapid thermal processing of printed CuIn nanoparticles and thermally evaporated selenium as precursor layer. Research is focused on real-time investigations such as in-situ X-ray diffraction and dynamic scanning calorimetry. These measurements show CISe formation starting at 300 C. Significant amount of intermediate phases as reported for state-of-the-art rapid thermal processing of stacked elemental layer was not observed. The morphology of the nanoparticulate layers was examined by field emission scanning electron microscopy. Grain size developed from nanosized binary CuIn nanoparticles to microsized CISe grains. Porosity decreases in the temperature range from 340 C to 540 C. © 2012 Elsevier B.V.



FAU-Autorinnen und Autoren / FAU-Herausgeberinnen und Herausgeber

Hock, Rainer Prof. Dr.
Professur für Kristallographie und Strukturphysik
Hölzing, Astrid
Professur für Kristallographie und Strukturphysik
Möckel, Stefan
Professur für Werkstoffwissenschaften (Werkstoffe der Elektrotechnik)
Wellmann, Peter Prof. Dr.-Ing.
Professur für Werkstoffwissenschaften (Werkstoffe der Elektrotechnik)


Zitierweisen

APA:
Möckel, S., Hölzing, A., Hock, R., & Wellmann, P. (2013). In-situ phase formation study of copper indium diselenide absorber layers from CuIn nanoparticles and evaporated selenium. Thin Solid Films, 535(1), 133-137. https://dx.doi.org/10.1016/j.tsf.2012.11.081

MLA:
Möckel, Stefan, et al. "In-situ phase formation study of copper indium diselenide absorber layers from CuIn nanoparticles and evaporated selenium." Thin Solid Films 535.1 (2013): 133-137.

BibTeX: 

Zuletzt aktualisiert 2018-07-08 um 21:41

Link teilen