Hydration kinetics of CA2 and CA - Investigations performed on a synthetic calcium aluminate cement

Beitrag in einer Fachzeitschrift


Details zur Publikation

Autorinnen und Autoren: Klaus S, Neubauer J, Götz-Neunhoeffer F
Zeitschrift: Cement and Concrete Research
Verlag: Elsevier
Jahr der Veröffentlichung: 2013
Heftnummer: 43 (1)
Seitenbereich: 62-69
ISSN: 0008-8846


Abstract


Much is already known about the hydration of monocalcium aluminate (CA) in calcium aluminate cements (CACs). CA2 is known to be weakly hydraulic. Therefore, the hydration kinetics of CA2 were not of as great interest as those of the hydration of CAC. We were able to show that the hydration of CA2 begins as soon as the hydration rate of CA has reached its maximum and the first precipitation of C2AH8 has started. The hydration of different CA/CA2 ratios was analyzed by the G-factor quantification. The individual contributions of the phases CA and CA2 to the heat flow were calculated based on the amounts dissolved by applying thermodynamic data. The heat flow as calculated from XRD data was then compared with the measured heat flow. It obtained a good consistency between the two. The very pronounced influence of CA2 during hydration of CAC can be clearly demonstrated. © 2012 Elsevier Ltd. All rights reserved.



FAU-Autorinnen und Autoren / FAU-Herausgeberinnen und Herausgeber

Götz-Neunhoeffer, Friedlinde Prof. Dr.
Lehrstuhl für Mineralogie
Klaus, Sebastian
Lehrstuhl für Mineralogie
Neubauer, Jürgen apl. Prof. Dr.
Lehrstuhl für Mineralogie


Zitierweisen

APA:
Klaus, S., Neubauer, J., & Götz-Neunhoeffer, F. (2013). Hydration kinetics of CA2 and CA - Investigations performed on a synthetic calcium aluminate cement. Cement and Concrete Research, 43 (1), 62-69. https://dx.doi.org/10.1016/j.cemconres.2012.09.005

MLA:
Klaus, Sebastian, Jürgen Neubauer, and Friedlinde Götz-Neunhoeffer. "Hydration kinetics of CA2 and CA - Investigations performed on a synthetic calcium aluminate cement." Cement and Concrete Research 43 (1) (2013): 62-69.

BibTeX: 

Zuletzt aktualisiert 2018-09-07 um 08:23