A comparative structural study of wet and dried ettringite

Beitrag in einer Fachzeitschrift


Details zur Publikation

Autorinnen und Autoren: Renaudin G, Filinchuk Y, Neubauer J, Götz-Neunhoeffer F
Zeitschrift: Cement and Concrete Research
Verlag: Elsevier
Jahr der Veröffentlichung: 2010
Band: 40
Heftnummer: 3
Seitenbereich: 370-375
ISSN: 0008-8846


Abstract


Two different techniques were used to compare structural characteristics of "wet" ettringite (stored in the synthesis mother liquid) and "dried" ettringite (dried to 35% relative humidity over saturated CaCl2 solution). Lattice parameters and the water content in the channel region of the structure (site occupancy factor of the water molecule not bonded to cations) as well as microstructure parameters (size and strain) were determined from a Rietveld refinement on synchrotron powder diffraction data. Local environment of sulphate anions and of the hydrogen bonding network was characterized by Raman spectroscopy. Both techniques led to the same conclusion: the "wet" ettringite sample immersed in the mother solution from the synthesis presents similar structural features as ettringite dried to 35% relative humidity. An increase of the a lattice parameter combined with a decrease of the c lattice parameter occurs on drying. The amount of structural water, the point symmetry of sulphate and the hydrogen bond network are unchanged when passing from the wet to the dried ettringite powder. Ettringite does not form a high-hydrate polymorph in equilibrium with alkaline solution, in contrast to the AFm phases that lose water molecules on drying. According to these results we conclude that ettringite precipitated in aqueous solution at the early hydration stages is of the same chemical composition as ettringite present in the hardening concrete. © 2009 Elsevier Ltd. All rights reserved.



FAU-Autorinnen und Autoren / FAU-Herausgeberinnen und Herausgeber

Götz-Neunhoeffer, Friedlinde Prof. Dr.
Lehrstuhl für Mineralogie
Neubauer, Jürgen apl. Prof. Dr.
Lehrstuhl für Mineralogie


Einrichtungen weiterer Autorinnen und Autoren

European Synchrotron Radiation Facility (ESRF)
Université d'Auvergne Clermont-Ferrand I / University of Auvergne


Zitierweisen

APA:
Renaudin, G., Filinchuk, Y., Neubauer, J., & Götz-Neunhoeffer, F. (2010). A comparative structural study of wet and dried ettringite. Cement and Concrete Research, 40(3), 370-375. https://dx.doi.org/10.1016/j.cemconres.2009.11.002

MLA:
Renaudin, G., et al. "A comparative structural study of wet and dried ettringite." Cement and Concrete Research 40.3 (2010): 370-375.

BibTeX: 

Zuletzt aktualisiert 2018-07-08 um 03:29