SILICONBORONOXYCARBIDE (SIBOC) FOAM FROM METHYL BOROSILOXANE

Beitrag in einer Fachzeitschrift


Details zur Publikation

Autorinnen und Autoren: Krishnan S, Fey T, Greil P
Zeitschrift: Ceramic Transactions
Verlag: American Ceramic Society
Jahr der Veröffentlichung: 2014
Band: 243
Seitenbereich: 47-60
ISSN: 1042-1122


Abstract


Siliconboronoxycarbide (SiBOC) foams were prepared from borosiloxane precursors by sacrificial pu foam template method. Methyl borosiloxane oligomer was synthesized from boric acid and methyltriethoxysilane. This SiBOC precursor (methylborosiloxane) was pyrolyzed at 1000 degrees C in argon with a ceramic yield of amorphous SiBOC of similar to 78%. Compressive strength of the foam sample achieved values of 410kPa at a total porosity of 85% and a mean pore cell diameter of approx. 700 mu p.. Annealing at 1400 degrees C in argon resulted in beta-SiC crystallization and a SiC/SiBOC nano composite foam was formed.



FAU-Autorinnen und Autoren / FAU-Herausgeberinnen und Herausgeber

Fey, Tobias Dr.
Lehrstuhl für Werkstoffwissenschaften (Glas und Keramik)
Greil, Peter Prof. Dr.
Lehrstuhl für Werkstoffwissenschaften (Glas und Keramik)


Zusätzliche Organisationseinheit(en)
Exzellenz-Cluster Engineering of Advanced Materials


Forschungsbereiche

E Lightweight Materials
Exzellenz-Cluster Engineering of Advanced Materials


Zitierweisen

APA:
Krishnan, S., Fey, T., & Greil, P. (2014). SILICONBORONOXYCARBIDE (SIBOC) FOAM FROM METHYL BOROSILOXANE. Ceramic Transactions, 243, 47-60.

MLA:
Krishnan, Sreejith, Tobias Fey, and Peter Greil. "SILICONBORONOXYCARBIDE (SIBOC) FOAM FROM METHYL BOROSILOXANE." Ceramic Transactions 243 (2014): 47-60.

BibTeX: 

Zuletzt aktualisiert 2018-10-08 um 02:39

Link teilen