Influence of solidification conditions on TCP phase formation, casting porosity and high temperature mechanical properties in a Re-containing nickel-base superalloy with columnar grain structure

Beitrag bei einer Tagung
(Konferenzbeitrag)


Details zur Publikation

Autor(en): Volek A, Singer R
Herausgeber: K. Green, H. Harada, T.E. Howson, T.M. Pollock, R.C. Reed, J.J. Schirra, S. Walston
Verlag: Minerals, Metals and Materials Society
Jahr der Veröffentlichung: 2004
Tagungsband: Superalloys 2004: Proceedings of the 10th Intenational Symposium of Superalloys
Seitenbereich: 713-718
Sprache: Englisch


Abstract


A coarse and a fine dendrite structure were produced using the newly developed DS-superalloy ExAl7 (≅ IN792 with 2-3 wt.-% Re) by changing the conditions of directional solidification. The two microstructures differed in their primary dendrite arm spacing by a factor of 1.6. During aging, very fine TCP phase precipitates (length approximately 20 μm, volume fraction ∼ 1%) were precipitated in the dendrite core, where the refractory element content was particularly high due to segregation. The finer dendrite structure resulted in a lesser tendency for TCP phase formation and smaller (but more numerous) casting pores. Creep strength was not affected by the dendrite size, apparently because TCP phase size and amount were still so small. Fatigue strength, however, was much improved by the finer dendrite structure. Casting pores were found to be somewhat larger than the TCP phases under the conditions investigated and to act as crack starters in fatigue.



FAU-Autoren / FAU-Herausgeber

Singer, Robert Prof. Dr.-Ing.
Lehrstuhl für Werkstoffwissenschaften (Werkstoffkunde und Technologie der Metalle)


Zitierweisen

APA:
Volek, A., & Singer, R. (2004). Influence of solidification conditions on TCP phase formation, casting porosity and high temperature mechanical properties in a Re-containing nickel-base superalloy with columnar grain structure. In K. Green, H. Harada, T.E. Howson, T.M. Pollock, R.C. Reed, J.J. Schirra, S. Walston (Eds.), Superalloys 2004: Proceedings of the 10th Intenational Symposium of Superalloys (pp. 713-718). Seven Springs, US: Minerals, Metals and Materials Society.

MLA:
Volek, Andreas, and Robert Singer. "Influence of solidification conditions on TCP phase formation, casting porosity and high temperature mechanical properties in a Re-containing nickel-base superalloy with columnar grain structure." Proceedings of the 10th International Symposium on Superalloys, SUPERALLOYS 2004, Seven Springs Ed. K. Green, H. Harada, T.E. Howson, T.M. Pollock, R.C. Reed, J.J. Schirra, S. Walston, Minerals, Metals and Materials Society, 2004. 713-718.

BibTeX: 

Zuletzt aktualisiert 2018-05-12 um 13:50