In-situ XRD investigation of re-crystallization and selenization of CZTS nanoparticles

Beitrag in einer Fachzeitschrift

Details zur Publikation

Autorinnen und Autoren: Sayed MH, Brandl M, Chory C, Hammer-Riedel I, Parisi J, Guetay L, Hock R
Zeitschrift: Journal of Alloys and Compounds
Jahr der Veröffentlichung: 2016
Band: 686
Seitenbereich: 24-29
ISSN: 0925-8388


Cu2ZnSnS4 nanoparticles have been produced by a facile and high-yield wet-chemical method at low synthesis temperature. In order to remove the organic residues the synthesis was followed by a pre-annealing procedure at 250 degrees C in nitrogen atmosphere. Data evaluation of ex-situ XRD measurements on the pre-annealed sample showed, that the diffraction pattern of the as-synthesized powder can be well modeled by diffraction of a hexagonal and a disordered cubic CZTS structure. The CZTS nanoparticles were annealed under nitrogen atmosphere up to 550 degrees C without and with the addition of selenium powder and diffraction patterns were recorded in-situ as a function of temperature in order to investigate the structural phase transitions during the re-crystallization and selenization of the powders. The in-situ XRD measurements showed a structural phase transition into the tetragonal CZTS structure for pure CZTS and with the addition of selenium. With the addition of selenium, an exchange reaction between sulfur and selenium during the heating process was observed by the shift in the diffraction peaks and subsequent refinement of the lattice parameters of the crystal structures. (C) 2016 Elsevier B.V. All rights reserved.

FAU-Autorinnen und Autoren / FAU-Herausgeberinnen und Herausgeber

Brandl, Marco
Lehrstuhl für Kristallographie und Strukturphysik
Hock, Rainer Prof. Dr.
Professur für Kristallographie und Strukturphysik

Einrichtungen weiterer Autorinnen und Autoren

Carl von Ossietzky Universität Oldenburg


Sayed, M.H., Brandl, M., Chory, C., Hammer-Riedel, I., Parisi, J., Guetay, L., & Hock, R. (2016). In-situ XRD investigation of re-crystallization and selenization of CZTS nanoparticles. Journal of Alloys and Compounds, 686, 24-29.

Sayed, Mohamed H., et al. "In-situ XRD investigation of re-crystallization and selenization of CZTS nanoparticles." Journal of Alloys and Compounds 686 (2016): 24-29.


Zuletzt aktualisiert 2018-10-08 um 15:24