Effect of B, Zr, and C on Hot Tearing of a Directionally Solidified Nickel-Based Superalloy

Beitrag in einer Fachzeitschrift
(Originalarbeit)


Details zur Publikation

Autor(en): Grodzki J, Hartmann N, Rettig R, Affeldt E, Singer R
Zeitschrift: Metallurgical and Materials Transactions A-Physical Metallurgy and Materials Science
Verlag: Springer Boston
Jahr der Veröffentlichung: 2016
Band: 47
Heftnummer: 6
Seitenbereich: 2914-2926
ISSN: 1073-5623
Sprache: Englisch


Abstract


The effect of the minor elements B, Zr, and C on the castability of a Nickel-based γ′-strengthened superalloy has been investigated. Tube-like specimens were prepared by directional solidification where the rigid ceramic core leads to hoop stresses and grain boundary cracking. It was found that an important improvement in castability can be achieved by adjusting the minor elemental composition. Too low C (≤0.15 pct) and too high B and Zr contents (≥0.05 pct) lead to material that is very prone to solidification cracking and should be avoided. The results cannot be rationalized on the basis of the current models for solidification cracking. Instead, pronounced hot tearing is observed to occur at high amounts of γ/γ′-eutectic and high Zr contents. The critical film stage where dendrites at the end of solidification do not touch and are separated by thin liquid films must be avoided. How Zr promotes the film stage will be discussed in the paper.



FAU-Autoren / FAU-Herausgeber

Grodzki, Jacek
Lehrstuhl für Werkstoffwissenschaften (Werkstoffkunde und Technologie der Metalle)
Hartmann, Nadine
Lehrstuhl für Werkstoffwissenschaften (Werkstoffkunde und Technologie der Metalle)
Rettig, Ralf Dr.-Ing.
Lehrstuhl für Werkstoffwissenschaften (Werkstoffkunde und Technologie der Metalle)
Singer, Robert Prof. Dr.-Ing.
Lehrstuhl für Werkstoffwissenschaften (Werkstoffkunde und Technologie der Metalle)


Zitierweisen

APA:
Grodzki, J., Hartmann, N., Rettig, R., Affeldt, E., & Singer, R. (2016). Effect of B, Zr, and C on Hot Tearing of a Directionally Solidified Nickel-Based Superalloy. Metallurgical and Materials Transactions A-Physical Metallurgy and Materials Science, 47(6), 2914-2926. https://dx.doi.org/10.1007/s11661-016-3416-8

MLA:
Grodzki, Jacek, et al. "Effect of B, Zr, and C on Hot Tearing of a Directionally Solidified Nickel-Based Superalloy." Metallurgical and Materials Transactions A-Physical Metallurgy and Materials Science 47.6 (2016): 2914-2926.

BibTeX: 

Zuletzt aktualisiert 2018-21-11 um 13:50