Influence of Ti and Zn on particle incorporation of AlB2, B and B4C particles in aluminum using the stir casting process

Beitrag in einer Fachzeitschrift
(Report)


Details zur Publikation

Autor(en): Plötz S, Lohmüller A, Singer R
Zeitschrift: Key Engineering Materials
Verlag: Trans Tech Publications Ltd
Jahr der Veröffentlichung: 2017
Band: 742
Seitenbereich: 173-180
ISBN: 9783035711981
ISSN: 1013-9826
Sprache: Englisch


Abstract


The outstanding performance of many aluminum matrix composites (AMCs) regarding specific stiffness makes AMCs attractive materials for lightweight construction. Low density boride compounds promise both an increase in stiffness and decrease in composite density. Therefore for this study AlB2, B and B4C were chosen for composite manufacturing. The composites were fabricated with the stir casting process. To avoid gas entrapment during mixing and ensure nonporous composites, partial vacuum was adapted during particle feeding and stirring. Poor wettability of used particle material in contact with liquid aluminum hindered particle incorporation, but alloying elements such as titanium were shown to affect wettability and particle incorporation for B4C. Zn had no influence on wettability or reactivity and did not improve particle incorporation. In contrast to Zn, Ti improved adhesion and wettability, but particle incorporation was improved exclusively for B4C. Besides alloying Ti, the use of high-shear force mixers improved particle incorporation enabling uniform particle distribution. AMCs with up to 12 vol.% of B4C particles were produced via stir casting without alloying Ti.



FAU-Autoren / FAU-Herausgeber

Lohmüller, Andreas
Lehrstuhl für Werkstoffwissenschaften (Werkstoffkunde und Technologie der Metalle)
Plötz, Steven
Zentralinstitut für Neue Materialien und Prozesstechnik
Singer, Robert Prof. Dr.-Ing.
Lehrstuhl für Werkstoffwissenschaften (Werkstoffkunde und Technologie der Metalle)


Zitierweisen

APA:
Plötz, S., Lohmüller, A., & Singer, R. (2017). Influence of Ti and Zn on particle incorporation of AlB2, B and B4C particles in aluminum using the stir casting process. Key Engineering Materials, 742, 173-180. https://dx.doi.org/10.4028/www.scientific.net/KEM.742.173

MLA:
Plötz, Steven, Andreas Lohmüller, and Robert Singer. "Influence of Ti and Zn on particle incorporation of AlB2, B and B4C particles in aluminum using the stir casting process." Key Engineering Materials 742 (2017): 173-180.

BibTeX: 

Zuletzt aktualisiert 2018-03-10 um 14:50