Aluminum-aluminum compound castings by electroless deposited zinc layers
Journal article
(Original article)
Publication Details
Author(s): Körner C, Schwankl M, Himmler D
Journal: → Journal of Materials Processing Technology |
Publication year: 2014
Volume: 214
Journal issue: 5
Pages range: 1094-1101
ISSN: 0924-0136
Language: English
Abstract
Sandblasted aluminum sheets (Al 99.5) were coated with a basic zincate solution and integrated into high pressure die casting components (AlSi9Cu3(Fe)) with wall thickness ranging from 3 mm to 6 mm. Investigations of the Al-Al-interface showed that sound castings could be realized. Microprobe analysis was used to elucidate the dissolution and diffusion of the Zn coating as a function of the processing parameters. Due to the very small total amount of zinc we did not find a zone of brittle intermetallic phases at the interface. Shear testing of the compounds confirmed the presence of a firmly bonded compound without embrittlement by intermetallic phases. © 2014 Elsevier B.V.
FAU Authors / FAU Editors
| Körner, Carolin Prof. Dr.-Ing. |
| | Lehrstuhl für Werkstoffwissenschaften (Werkstoffkunde und Technologie der Metalle) |
|
| | | Lehrstuhl für Werkstoffwissenschaften (Werkstoffkunde und Technologie der Metalle) |
|
How to cite
APA: | Körner, C., Schwankl, M., & Himmler, D. (2014). Aluminum-aluminum compound castings by electroless deposited zinc layers. Journal of Materials Processing Technology, 214(5), 1094-1101. https://dx.doi.org/10.1016/j.jmatprotec.2013.12.014 |
MLA: | Körner, Carolin, Matthias Schwankl, and David Himmler. "Aluminum-aluminum compound castings by electroless deposited zinc layers." Journal of Materials Processing Technology 214.5 (2014): 1094-1101. |