Analysis of Compensation Effects in Aluminum-Implanted 4H-SiC Devices

Weiße J, Hauck M, Sledziewski T, Tschiesche M, Krieger M, Bauer A, Mitlehner H, Frey L, Erlbacher T (2018)


Publication Language: English

Publication Type: Journal article, Report

Publication year: 2018

Journal

Edited Volumes: Materials Science Forum

Book Volume: 924

Pages Range: 184-187

DOI: 10.4028/www.scientific.net/MSF.924.184

Abstract

In this work, we analyze compensating defects which are formed after implantation of aluminum (Al) into n-type 4H-SiC epitaxial layers and subsequent thermal annealing. These defects reduce the expected free charge carrier density by 84% for a low doped layer with [Al]impl ≈ 9ž·1016 cm-3 and by 27 % for a high doped layer with [Al]impl ≈ 2·ž1019 cm-3. Furthermore, an electrical activation ratio of implanted aluminum ions of 100 % is calculated. The ionization energy of implanted aluminum as measured by Hall effect and admittance spectroscopy ranges from 101 meV to 305 meV depending on the doping concentration.

Authors with CRIS profile

Related research project(s)

Involved external institutions

How to cite

APA:

Weiße, J., Hauck, M., Sledziewski, T., Tschiesche, M., Krieger, M., Bauer, A.,... Erlbacher, T. (2018). Analysis of Compensation Effects in Aluminum-Implanted 4H-SiC Devices. Materials Science Forum, 924, 184-187. https://dx.doi.org/10.4028/www.scientific.net/MSF.924.184

MLA:

Weiße, Julietta, et al. "Analysis of Compensation Effects in Aluminum-Implanted 4H-SiC Devices." Materials Science Forum 924 (2018): 184-187.

BibTeX: Download