Influence of surface roughness on the tribological properties of HF-CVD diamond coated heat-treatable steel

Kellermann K, Erhardt S, Fandrey J, Rosiwal S, Singer R (2010)


Publication Language: English

Publication Status: Published

Publication Type: Journal article

Publication year: 2010

Journal

Publisher: ELSEVIER SCIENCE SA

Book Volume: 269

Pages Range: 811-815

Journal Issue: 11-12

DOI: 10.1016/j.wear.2010.08.009

Abstract

Standard heat-treatable C35 (1 0501) steel specimens were pre-coated with diffusion chromium carbide interlayer and in second step a crystalline diamond film was applied by Hot-Filament Chemical Vapour Deposition This study investigates the tribological properties of specimens that were treated mechanically in a different way before the coating in order to achieve a different roughness The tests were performed in a water lubricated ring-on-disc configuration while the coefficient of friction was measured Wear analysis was done by light microscope The wear development was obtained by several stops during testing The friction and wear developments are compared and discussed for different surface roughness Pre-treatment of the steel surface has a great influence on the tribological properties of the CVD diamond coating especially the evenness of the surface determines the real contact area and therefore the wear behavior (C) 2010 Elsevier B V All rights reserved

Authors with CRIS profile

Related research project(s)

How to cite

APA:

Kellermann, K., Erhardt, S., Fandrey, J., Rosiwal, S., & Singer, R. (2010). Influence of surface roughness on the tribological properties of HF-CVD diamond coated heat-treatable steel. Wear, 269(11-12), 811-815. https://dx.doi.org/10.1016/j.wear.2010.08.009

MLA:

Kellermann, Karsten, et al. "Influence of surface roughness on the tribological properties of HF-CVD diamond coated heat-treatable steel." Wear 269.11-12 (2010): 811-815.

BibTeX: Download